Instructions
● Alkali - free glass fiber woven by high - temperature treatment surface by organic silicon copolymer tree coating processing
● High temperature resistant (200℃)
● High pressure resistant
● Flame retardant UL1441 VW-1
● Good mechanical properties
● Good insulation
● Good softness
● Through UL
Application
Widely used in class H insulation motor, household appliances insulation, electrical insulation and so on.
Specifications
|
Property
|
Indicators
|
|
Bending property after heating
|
Coating no visible cracking or peeling, primary color is clearly visible. The test temperature was 260±5℃ and 48±1 h.
|
|
Bending at low temperature
|
Coating no visible cracking or peeling, primary color is clearly visible. Test temperature -70±5℃, 60±10 hours.
|
|
Flame retardancy
|
For a maximum of 60 seconds, flags for any of the three trials should not be burned, and burning or hot particles should not ignite the cotton.
|
|
Temperature index with a thermal life of 20,000 hours
|
200℃
|
|
The standard diameter(mm)
|
Inside diameter tolerance(mm)
|
Wall thickness(mm)
|
Packaging
|
|
m/roll
|
m/plate
|
|
0.5
|
+0.1
|
0.18
|
100
|
1000
|
|
0.8
|
+0.1
|
0.18
|
100
|
1000
|
|
1.0
|
+0.1
|
0.18
|
100
|
1000
|
|
1.5
|
+0.2
|
0.18
|
100
|
1000
|
|
2.0
|
+0.2
|
0.18
|
100
|
600
|
|
2.5
|
+0.2
|
0.18
|
100
|
500
|
|
3.0
|
+0.3
|
0.23
|
100
|
400
|
|
3.5
|
+0.3
|
0.23
|
100
|
200
|
|
4.0
|
+0.3
|
0.23
|
100
|
200
|
|
4.5
|
+0.3
|
0.28
|
100
|
200
|
|
5.0
|
+0.4
|
0.28
|
100
|
200
|
|
5.5
|
+0.4
|
0.28
|
100
|
200
|
|
6.0
|
+0.4
|
0.32
|
100
|
200
|
|
7.0
|
+0.6
|
0.32
|
100
|
100
|
|
8.0
|
+0.6
|
0.32
|
50
|
100
|
|
9.0
|
+0.6
|
0.32
|
50
|
100
|
|
10
|
+0.8
|
0.52
|
50
|
100
|
|
11
|
+0.8
|
0.52
|
25
|
100
|
|
12
|
+0.8
|
0.52
|
25
|
100
|
|
13
|
+0.8
|
0.52
|
25
|
|
|
14
|
+0.8
|
0.52
|
25
|
|
|
15
|
+0.8
|
0.52
|
25
|
|
|
16
|
+0.8
|
0.52
|
20
|
|
|
18
|
+0.8
|
0.52
|
20
|
|
|
20
|
+0.8
|
0.52
|
20
|
|
|
25
|
+0.8
|
0.52
|
20
|
|
|
30
|
+0.8
|
0.52
|
20
|
|